SILICONE
RUBBER
 |
|
|
|
TSE
221-3U |
| GENERAL
PURPOSE MOLDING
|
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.08 |
| Appearance
|
Milky
white Translucent |
| William's
Plasticity(10 min after freshening) |
120 |
|
|
|
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
|
|
|
Physical
Properties |
| Hardness
(JISA) |
30 |
| Tensile
strength kgf/cm2(MPa) |
66(6.5) |
| Elongation |
610 |
| Tear
strength kgf/cm (N/mm)(JISB) |
17(17) |
| Compression
Set.5% |
19 |
|
|
|
|
|
TSE
221-4U |
| GENERAL
PURPOSE MOLDING |
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.13 |
| Appearance
|
Milky
white Translucent |
| William's
Plasticity(10 min after freshening) |
170 |
|
|
|
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
|
|
|
Physical
Properties |
| Hardness
|
40 |
| Tensile
strength kgf/cm2(MPa) |
90(8.8) |
| Elongation |
530 |
| Tear
strength kgf/cm (N/mm)(JISB) |
22(22) |
| Compression
Set.5% |
19 |
|
|
|
|
TSE
221-5U |
| GENERAL
PURPOSE MOLDING |
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.15 |
| Appearance
|
Milky
white Translucent |
| William's
Plasticity(10 min after freshening) |
220 |
|
|
|
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
|
|
|
Physical
Properties |
| Hardness |
50 |
| Tensile
strength kgf/cm2(MPa) |
100(9.8) |
| Elongation |
390 |
| Tear
strength kgf/cm (N/mm)(JISB) |
23(23) |
| Compression
Set.5% |
19 |
|
|
|
|
TSE
221-6U |
| GENERAL
PURPOSE MOLDING |
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.25 |
| Appearance
|
Light
Gray |
| William's
Plasticity(10 min after freshening) |
240 |
|
|
|
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
|
|
|
Physical
Properties |
| Hardness
|
60 |
| Tensile
strength kgf/cm2(MPa) |
78(7.7) |
| Elongation |
270 |
| Tear
strength kgf/cm (N/mm)(JISB) |
18(18) |
| Compression
Set.5% |
19 |
|
|
|
|
TSE
221-7U |
| GENERAL
PURPOSE MOLDING |
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.30 |
| Appearance
|
Light
Gray |
| William's
Plasticity(10 min after freshening) |
280 |
|
|
|
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
|
|
|
Physical
Properties |
| Hardness
|
70 |
| Tensile
strength kgf/cm2(MPa) |
70(6.9) |
| Elongation |
220 |
| Tear
strength kgf/cm (N/mm)(JISB) |
17(17) |
| Compression
Set.5% |
19 |
|
|
|
|
TSE
221-8U |
| GENERAL
PURPOSE MOLDING |
| APPLICATIONS |
O-rings,
Gaskets, Diaphragms, Boots Sheets |
|
|
| TYPICAL
PRODUCT DATA |
|
Typical
Properties of Uncured Compound |
| Property |
Value |
| Specific
Gravity(25oC) |
1.42 |
| Appearance
|
Light
Gray |
| William's
Plasticity(10 min after freshening) |
350 |
|
| |
|
Typical
Properties of Cured Compounds |
| Curing
Agent |
0.5 |
| Cure
conditions |
170,10 |
| Post
Cure o C h |
200,4 |
|
| |
|
Physical
Properties |
|
Hardness
|
80 |
|
Tensile
strength kgf/cm2(MPa) |
61(6.0) |
|
Elongation |
200 |
|
Tear
strength kgf/cm (N/mm)(JISB) |
17(17) |
|
Compression
Set.5% |
18 |
|